MOMANSA 20-22

MOMANSA20-22 is a single component, high build chlorosulphonated rubber based, suitably plasticized self priming and top coat of various metals, wood and concrete. It is highly corrosion resistant, fast drying self primer and fire retardant coating. This product has excellent adhesion properties with good impact resistance. It can be used as a part of a system comprising a primer or top coat in areas exposed to atmospheric corrosion. These properties allow MOMANSA 20-22 to be used in a wide variety of industrial applications.

ADVANTAGES

  • Excellent Anti-corrosive property
  • Fire Retardant
  • Water Resistant
  • Excellent heat resistance
  • Chemical resistance
  • Excellent impact & abrasion resistance
  • Very easy application by brush & roller
  • Fast drying
  • Suitable for metal and concrete

USES

Suitable for use in both old and new steel tructure. It can be used as a top coat including kitchen and ventilation duct, offshore structures, petrochemical & chemical complexes, pipelines, fertilizers industries, MS Bridges, and power Industry etc

CONCRETE AND MASONRY

Remove all loose particles, oil, grease, form release agents and any other contaminants. New concrete and masonry must be allowed to cure for a minimum of 30days. Before painting, roughen the surface by abrasive blasting, acid etching or scarifying. The surface should be clean, dry and free from oil, grease and loose particles.

METHOD OFAPPLICATION

Generally MOMANSA 20-22 is best applied by brush and roller. Due to the rapid dry of this coating, areas may be coated by brush, applicator pad, or roller. Care must be taken to achieve the specified wet and dry film thicknesses. Uniform, even coats must be obtained. Large horizontal surfaces should be spray applied, however roller and brush application can be performed.

SURFACE PREPARATION METAL

All surfaces shall be free of loose rust, mill scale and contaminants such as oil, grease, dirt and salts. Before any surface preparation is attempted, oil and grease must be removed by Corrosion to remove mill scale, rust and other contaminants and leave a roughened surface.

COVERAGE

The coverage of MOMANSA20-22 may vary and depending upon surface condition, but MOMANSA 20-22 will give you approximate 8-2, 10 meter square per kg

APPLICATION MOOD

  • Spray– Use airless spray or conventional spray.
  • Brush- Recommended for all areas, care must be taken to achieve the specified DFT. 

MIXING

This is a single component product is mixed thoroughly till homogenous mixing. If the settling is observed, loosen the settled material with help of hand stirrer followed by power driven stirrer. For best results, use a spiral mixing blade at a variable speed (400-600 rpm).

CAUTION

Adequate ventilation must be maintained, particularly in confined spaces, due to volatile in nature.